Metallic Color Shining Pearl Color Aluminum Composite Panel

Metallic Color Shining Pearl Color Aluminum Composite Panel

Quick Details Size: 1220*2440*4*0.3mm Place of Origin: Shandong, China Brand Name: FAME Model Number: M0001 Usage: Outdoor Function: Anti-Static, Antibacterial, Fireproof Surface Treatment: Anodized, Brushed, Mirror, PE Coated, PVDF Coated Product name: metallic color shining pearl color aluminum composite panel Type: PE Coated Aluminum Composite Panels Color: Customer's Requirements Application: Curtain Wall/Decoration Protective film: OEM Accepted Standard size: 1220mm x 2440mm Pancel thickness: 2mm--6mm Aluminium foil thickness: 0.02mm-0.6mm Certificate: ISO9001

Send Inquiry Chat Now

Fast Delievery
Quality Assurance
24/7 Customer Service

Product Introduction

suit for south-east market outdoor wall cover

1)Aluminum skin thickness: 0.08mm-0.50mm.

2)Total panel thickness: 2mm-6mm.

3) Width:1000mm,1220mm (regular), 1250mm,1300mm,1500mm

4) Length:Up to 6500mm;

5) Standard size:1220mm(Width) ×2440mm(Length).

6)Surface Treatment:PVDF coating and PE coating.

7)Main aluminum composite wall panel Product:PE coated ACP,PVDF coated ACP,Nano PVDF coated ACP,Mirror finish ACP,Brushed ACP,Wooden ACP,Granite ACP and Fireproof core ACP.

8) Non-standard sizes and special colors are available depending on customers’ offers.

9)thickness of film:0.07mm/0.09mm

10)4700sqm/20GP

11)PE core or Fire-rated Core

1) Front Side: aluminum alloy sheet coated with fluoro-carbon resin(PVDF) or polyester resin (PE)

roasting painting

2) Core Material: nontoxic polyethylene, PE, FR, LDPE

3) Back Side: aluminum alloy sheet coated with polyester resin painting(PE)

Paint Thickness(micron)	Anodize
Pencil Hardness	2H
Toughness Of Coating	2T
Temperature Resistance	-50°C+90°C
Impact Strength(kg/cm2)	50
Boiling Water Resistance	boiling for 2 hours,No change
Acid Resistance	Immerse surface in 2% HC1 for 24hours,No change
Alkali Resistance	Immerse surface in 2% NAOH for 24hours,No change
Oil Resistance	Immerse surface in 20# engine oil for 24hours,No change
Solvent Resistance	Cleaned 100 times with Dimethylbenzene,No change
Cleaning Resistance	>1000 times no change
Thermal Expansion	2.4mm/m @100°C Temp difference
Peel Strength	Average 131N.mm/mm
Bending Strength	>100MPA
Bending Elastic Modules	>2.0*104MPA
Heat Distortion Temperature	>95°C